Alumina Dispersion Strengthened Copper C15760 Alumina Copper Rod Cu-Al2O3
Product Normal Description:
| Product Name | Alumina Copper Rod |
|---|---|
| Model No. | C15760 |
| Product Specification: | Custom specification is available upon request. |
| Available Products: | Round rods, bars, flat products |
| Delivery Time: | Usually within 10~15 days |
| Package: | Packed in woodencases |
| Brand Name: | CUBERYLLIUM® |
About CUBERYLLIUM®:
Hangzhou Cuberyllium Metal Technology Co.,Ltd. specialized in supplying beryllium copper alloys, high copper alloys, casting copper alloys, copper foil and other copper alloys. Our products have broadly been used in resistance welding, plastic injetion mold, aviation, shipbuilding, military industry, metallurgy, electronics industry and so on. We strive to offer high quality with competitive price due to our advanced technology and equipment.
Chemical Composition of Alumina Dispersion Strengthened Copper C15760:
Product Grade: CUBERYLLIUM ®-C15760 (RWMA Class 20)
| Aluminum | 0.60% by wt. as Al₂O₃ |
| Cu: | Balance |
Typical Physical Properties of Alumina Dispersion Strengthened Copper C15760:
| Melting Point | 1083°C | 1981°F |
| Density | 8.81 g/cm3 at 20°C | 0.318 lbs./in3 at 68°F |
| Electrical Conductivity (σ) | 0.452 μ Ω-cm at 20°C | 78% IACS at 68°F |
| Thermal Conductivity (K) | 322 W/m/K at 20°C | 186 Btu/ft2/ft/hr/°F at 68°F |
| Electrical Resistivity (ρ) | 2.21 μ Ω-cm at 20°C | 13.29 Ω circular-mil/ft. at 68°F |
| Coefficient of Thermal Expansion | 16.6 μm/m/°C (20-150°C) | 9.2 μin/in/°F (68-300°F) |
| Modulus of Elasticity (Tension) (λ) | 130 Gpa | 19 x 10⁶ psi |
Mechanical Properties of Alumina Dispersion Strengthened Copper C15760:
| Shapes | Thickness or Dia. | Temper | Tensile Strength | Yield Strength | Elongation | Hardness | |||
| mm | in | or Condition | MPa | ksi | MPa | ksi | % | HRB | |
|
Flat products | 10 | 0.400 | As Cons.* | 517 | 75 | 413 | 60 | 13 | 81 |
| 2.5 | 0.100 | CW**75% | 627 | 91 | 572 | 83 | 8 | 85 | |
| 0.15 | 0.006 | CW 98% | 737 | 107 | 655 | 95 | 6 | - | |
|
Rod | 14 | 0.54 | As Cons. | 551 | 80 | 517 | 75 | 22 | 80 |
| 13 | 0.5 | CW 14% | 572 | 83 | 544 | 79 | 16 | 83 | |
| 7 | 0.275 | CW 74% | 620 | 90 | 599 | 87 | 14 | 86 | |
| 64 | 2.5 | As Cons. | 496 | 72 | 475 | 69 | 4 | 80 | |
| Rounds | Up to 760 | 30 | As Cons. | 469 | 68 | 331 | 48 | 4 | 76 |
Applications of Alumina Dispersion Strengthened Copper C15760:
Cuberyllium C15760(RWMA Class 20) is primarily designed for applications requiring the highest elevated temperature strength coupled with relatively high electrical and thermal conductivities. It exhibits a high degree of resistance to softening after exposure to elevated temperatures. Cuberyllium C15760 has sufficient cold working charateristics for heading, extrusion and some drawing and rolling operations.
| Recommended for: | Resistance welding electrodes |
| Welding electrodes | |
| Solder gun tips and MIG contact tips |
For applications requiring brazed joints and /or extended high temperature exposure in hydrogen-containing atmospheres or vacuum, low Oxygen is availbale and recommended.